Cooling animals and animal fur with nanoparticles

ABSTRACT

Nanoparticle treated fibrous articles, such as fabrics, fibers, filaments, or yarns, include a plurality of exposed, nonionic metal nanoparticles non-covalently affixed thereto. Metal nanoparticles can be strongly affixed to fibrous articles without covalently bonds and/or without being encapsulated within a polymer or adhesive. Such metal nanoparticles appear to adhere to fibrous articles by Van der Waals forces. Because they are nonionic, the nanoparticles are not easily removed by solvents, water, surfactants, and soaps, and remain after several washings, sometimes up to 50 or more washings.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent applicationSer. No. 14/861,375, filed Sep. 22, 2015, which application claims thebenefit of U.S. Provisional Patent Application No. 62/054,182, filedSep. 23, 2014, the disclosures of each of which are incorporated hereinby this reference.

BACKGROUND 1. Field of the Invention

Disclosed herein are nanoparticle treated fibrous articles, such asfabrics, fibers, filaments, and yarns, compositions and methods formaking nanoparticle treated fibrous articles, and methods of usingnanoparticle treated fibrous articles.

2. Relevant Technology

Utilization of various nanoparticle materials into and/or onto fabricshas been used in an attempt to impart characteristic advantages of agiven nanoparticle to a given fabric. The term “nanoparticle” oftenrefers to particles of any shape having a largest dimension of less than100 nm. By way of example, silver (Ag) nanoparticles have been appliedto fabrics to provide antimicrobial, antibacterial, or other relatedproperties.

There are several notable problems with existing nanoparticle treatedfabrics. For example, without a mechanism for substantially permanentimmobilization of nanoparticles onto the fabric, any performanceenhancement provided by the nanoparticles is quickly lost. Conversely,if a completely permanent mechanism for nanoparticle immobilization ortethering is used, the characteristics of the nanoparticles can bealtered by such immobilization and their efficacy is limited as thenanoparticle is unable to freely interact as it otherwise would as asuspended, non-tethered particle. In addition, covalently bondingnanoparticles to fibers and fabric surfaces is very expensive. If,instead, the nanoparticles are merely encapsulated within a polymer orother binder material, they are generally unavailable for any purposeuntil the binder sloughs off, wears away, or otherwise exposes thenanoparticles.

The tradeoff between maintaining desired nanoparticle activity, on theone hand, and immobilizing the nanoparticles, on the other, has led tothe development of methods for permanently attaching metal nanoparticlesto fabrics and using the metal nanoparticles as a source of metalcations that provide the desired effects. This is particularly true inthe case of silver (Ag) nanoparticles. Examples include covalentlybonding nanoparticles onto the fibers as in U.S. Pat. No. 6,607,994,utilization of electrostatic interactions between the nanoparticles andthe fabric as in U.S. Pat. Pub. No. 2009/0098366, and growing silvernanoparticles on the fabric fiber surface as in U.S. Pat. Pub. No.2011/0110999 Immobilized silver (Ag) nanoparticles can in this wayproduce silver ions (Ag+) more rapidly than when using silver (Ag)threads or other macro-sized silver (Ag) components, and in asignificantly more controlled manner than impregnation of fabric withsilver (Ag) salts.

Regardless of the specific results or efficacy of any of these prior artsolutions, each ultimately relies upon the release of metal cations intothe local environment in order to provide any antimicrobial efficacy.Unfortunately, such metal cations, including heavy metal cations,ultimately make their way into the larger environment with undesirableconsequences because of their fundamentally and indiscriminately toxicnature.

Noticeably absent in the art is any known or proposed mechanism forapplying nanoparticles onto fibers in such a way that the desirednanoparticles remain adhered to the fibers until an active transportmechanism is presented that is capable of overcoming adhesive forcesholding the particles onto the fabric surface. Such releasable adhesionof the nanoparticles to the fabric fibers would allow the nanoparticlesto, at the appropriate time, go into solution without relying on amechanism of ion release to provide antimicrobial efficacy.

SUMMARY

Disclosed herein are nanoparticle treated fibrous articles, such asfabrics, fibers, filaments, and yarns having antimicrobial properties,and related methods of manufacturing and using nanoparticle treatedfibrous articles. Treated fibers may be natural or synthetic. Naturalfibers include animal hair or fur. Accordingly, the scope of the presentdisclosure includes treating an animal with nonionic metal nanoparticlesby applying the nanoparticles to the animal's hair or fur.

The nanoparticle treated fibrous articles, such as fabrics, fibers,filaments, and yarns, can include metal nanoparticles affixed thereto,such as spherical-shaped nanoparticles that can remain strongly affixedto the fabric, fiber, filament, or yarn surface without covalent bonds,without ionic bonds, and without being encapsulated by a polymer oradhesive. The spherical-shaped nanoparticles resist being washed out byconventional laundering or cleaning methods that utilize one or more ofwater, solvents, soaps, detergents, surfactants, and mechanicalagitation. Nevertheless, when nanoparticles are contacted by a microbethey can be released into the microbes (e.g., by active absorption orother transport mechanism) and then kill or denature the microbes.Non-spherical nanoparticles, such as coral-shaped nanoparticles, can beused, preferably together with spherical-shaped nanoparticles.

According to some embodiments, nanoparticles can be releasably affixedto fibrous articles such that they adhere to the fibrous articles duringnormal use but are nonetheless available to microbes such as viruses,bacteria, and fungi. Because neither the nanoparticles nor thecombination of the nanoparticles affixed to fibrous articles demonstratesignificant cation production, but silver (Ag) nanoparticles affixed tothe fibers or fabrics nonetheless demonstrate substantial antimicrobialefficacy, it is postulated that the nanoparticles are releasably affixedto the fibrous articles until an active absorption or other transportmechanism, such as provided by bacteria, causes their removal. Becausenanoparticles can strongly adhere to fibrous articles, such as fabrics,fibers, filaments, and yarns, without covalent bonds, ionic bonds, orphysical incorporation into a polymer or adhesive, it follows that theadhesive forces that strongly affix the nanoparticles to the fibrousarticles are Van der Waals forces.

A non-limiting example of a nanoparticle treated fibrous articlecomprises: (1) a fabric, fiber, filament, or yarn and (2) a plurality ofexposed, nonionic metal nanoparticles non-covalently affixed to thefabric, fiber, filament, or yarn. An “exposed” nanoparticle is one thatis not encapsulated within another substance, such as a polymer oradhesive.

A non-limiting example of method of manufacturing a nanoparticle treatedfibrous article comprises: (1) applying a nanoparticle compositioncomprised of a liquid carrier and a plurality of non-ionic metalnanoparticles to a fibrous article, such as a fabric, fiber, filament,or yarn, and (2) removing the liquid carrier to yield a nanoparticletreated fibrous articles in which the nonionic metal nanoparticles areexposed and non-covalently affixed to the fibrous articles.

A non-limiting example of method of a method of using a nanoparticletreated fibrous article comprises: (1) providing a nanoparticle treatedfibrous article composed of (a) a fabric, fiber, filament, or yarn and(b) a plurality of exposed, nonionic metal nanoparticles non-covalentlyaffixed to the fabric, fiber, filament, or yarn; (2) exposing thenanoparticle treated fibrous article to microbes; (3) the microbesselectively removing a portion of the exposed, nonionic metalnanoparticles from the fibrous article; and (4) the metal nanoparticleskilling or denaturing the microbes.

In some embodiments, a nanoparticle treated material exhibits anti-odorproperties. For example, some embodiments include a plurality of silvernanoparticles providing anti-microbial functionality (which reduces oreliminates microbial production of odor causing molecules) and aplurality of gold nanoparticles providing an additional, independentsource of anti-odor functionality (e.g., by catalyzing the disruption orbreakdown of amines, sulfides, organic molecules, and other odorousmolecules).

In some embodiments, a nanoparticle treated material exhibits improveddurability and colorfast properties. For example, some embodimentsinclude a plurality of nanoparticles (e.g., gold nanoparticles)configured to induce a phase shift (e.g., toward the red end of thespectrum) of ultraviolet (UV) light (e.g., from sunlight) incident uponthe treated material. The associated protection from ultraviolet lightcan beneficially improve the strength, durability, and color-fastness ofthe nanoparticle treated material.

In some embodiments, a nanoparticle treated material exhibits improveddrying/moisture removal properties. For example, the nanoparticles of ananoparticle treated material can provide an increased surface area fordrying and/or can alter the emissivity of the treated material, therebyleading to greater removal of moisture from the treated material.

Increasing emissivity can also yield a fabric or material that radiatesor loses heat more quickly and feels cooler to the touch. In certainembodiments, a nanoparticle composition is applied to fibers which arein the form of an animal's fur or hair. The application of nanoparticlesto the animal's fur or hair may beneficially cool the animal. Forexample, it has been found that by applying a nanoparticle compositionto the hair of cattle can cool the cattle and thereby reduce oreliminate detrimental effects of heat-induced stress. Such nanoparticlecompositions may be formulated according to any of the embodimentsdescribed herein (e.g., with respect to size range, size distribution,shape, and type of metal used). Presently preferred embodiments includea carrier with spherical-shaped and/or coral-shaped, gold nanoparticles.Some quantity of the applied nanoparticles may also contact the animal'sskin and provide a cooling effect thereto.

In some embodiments, a nanoparticle treated material exhibits radiationprotection properties. For example, some embodiments include a pluralityof nanoparticles (e.g., beryllium and/or gold) configured to absorbharmful radiation (e.g., alpha particles, beta particles, and/or gammaradiation), thereby reducing or eliminating an amount of radiationpassing through the nanoparticle treated material.

In some embodiments, a nanoparticle treated material decreases oreliminates visibility to radar, infrared, and/or other detectionmethods. For example, some embodiments include a plurality ofnanoparticles (e.g., cobalt nanoparticles) configured to absorb radarand/or other detection signals, thereby rendering the nanoparticletreated material invisible or less visible to detection.

In some embodiments, a nanoparticle treated material is formed as anelectrically conductive material. For example, a plurality of conductivemetal nanoparticles can be embedded within a fibrous article to providethe fibrous article with electrically conductive properties. Theconductive properties can be tuned by adjusting the type and compositionof the nanoparticles used, the concentration of the nanoparticles,and/or the distribution of nanoparticles throughout the fibrous article,for example. In one embodiment, a conductive fibrous article can be usedin applications for detecting a break in a fiber and/or the level ofbreakage in a collection of fibers based on changes in conductivity ofthe material.

In some embodiments, a plurality of nanoparticles can be added to amasterbatch prior to processing of the masterbatch into fibers, fabrics,upholsteries, yarns, filaments, etc. (e.g., for polyesters, nylons,acrylics, and other synthetic fabrics). In such embodiments, thenanoparticles added to the masterbatch can be embedded in the resultingfabric. In some embodiments, the nanoparticles may be added to themasterbatch by mixing the nanoparticles in an ethylene glycol carrier orsimilar carrier (e.g., other alcohols and particularly other diols), andadding the resulting solution to the masterbatch. The resulting solutioncan have a concentration of nanoparticles with a lower bound of about 1ppm, 3 ppm, 5 ppm, 10 ppm, 15 ppm, or 25 ppm, and an upper bound ofabout 50 ppm, 100 ppm, 200 ppm, 300 ppm, 400 ppm, or 500 ppm, or mayhave a concentration within a range of any of the foregoing upper andlower bounds, for example.

These and other advantages and features of the invention will be setforth in part in the description which follows, and in part will becomeapparent to those skilled in the art upon examination of the followingor may be learned by practice of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a transmission electron microscope image (TEM) of exemplaryspherical-shaped metal nanoparticles having substantially uniform sizeand narrow particle size distribution for use in treating fibrousarticles;

FIGS. 2A-2E are transmission electron microscope images (TEMs) ofexemplary coral-shaped metal nanoparticles for use in treating fibrousarticles;

FIG. 3 schematically illustrates a fibrous article surface and aplurality of spherical-shaped nanoparticles affixed thereto;

FIG. 4 is a theoretical model showing a spherical-shaped metalnanoparticle strongly affixed to a fibrous article surface withoutcovelent or ionic bonds;

FIG. 5 schematically illustrates a microbe approaching a fibrous articlesurface and removing a portion of the spherical-shaped nanoparticles;

FIG. 6 schematically illustrates a microbe protein with disulfide bondsbeing catalytically denatured by an adjacent spherical-shapednanoparticle; and

FIG. 7 schematically illustrates a mammalian protein with disulfidebonds that are shielded so as to resist being catalytically denatured byan adjacent spherical-shaped nanoparticle.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Fibrous articles, such as fabrics, fibers, filaments, and yarns, can betreated with nonionic metal nanoparticles in order to impartantimicrobial properties and/or other desired attributes such as heattransfer properties. Any known fabric, fiber, filament, or yarn can betreated with nonionic metal nanoparticles, such as those made fromnatural or synthetic materials. Natural fibers include animal hair orfur or even feathers. Accordingly, the scope of the present disclosureincludes treating an animal with nonionic metal nanoparticles byapplying the nanoparticles to the animal's hair, fur, or feathers, asthe case may be. Treated animals may include livestock animals (e.g.,cattle, pigs, sheep, goats, horses, rabbits, chickens, turkeys, etc.),pets, zoo animals, wildlife, or other animal in need of cooling.

According to some embodiments, a nanoparticle treated fibrous articlecomprises (1) a fabric, fiber, filament, or yarn and (2) a plurality ofexposed, nonionic metal nanoparticles non-covalently affixed to thefabric, fiber, filament, or yarn. An “exposed” nanoparticle is one thatis not encapsulated within another substance, such as a polymer oradhesive. The fibrous articles may comprise any known fibrous material,such as organic fibers. Examples include natural fibers (e.g., a widevariety of plant fibers or even animal derived fibers, such as animalfur or hair on or removed from of the animal) and synthetic fibers(e.g., made from a wide variety of synthetic polymers known in the art).

Nonionic metal nanoparticles can be non-covalently affixed to fibrousarticles by Van der Waals forces and can remain affixed to the fibrousarticle when exposed to water, soaps, surfactants, and solvents butselectively removed when contacted by a microbe such as a virus,bacterium or fungus. In some embodiments, spherical-shaped metalnanoparticles can be strongly affixed to fibrous article surfaces by Vander Waals forces. Similarly, Van der Waals forces can also act to adherecoral-shaped nanoparticles to fibrous article surfaces although perhapsnot as strongly as spherical-shaped nanoparticles.

According to some embodiments, a nanoparticle treated fibrous articlecomprises (1) a fabric, fiber, filament, or yarn and (2) a plurality ofembedded, nonionic metal nanoparticles. For example, the metalnanoparticles can be added to a masterbatch prior to processing of themasterbatch into a fibrous article.

Nanoparticle Configurations

Nanoparticles that have been found to be particularly useful in treatingfibrous articles, such as fabrics, fibers, filaments, and yarns, includespherical-shaped metal nanoparticles, particularly sphericalnanoparticles having diameters of about 40 nm or less, and especiallyspherical nanoparticles having a narrow particle size distribution.Examples of spherical-shaped metal nanoparticles and methods and systemsfor manufacturing essentially spherical nanoparticles having controlledparticle sizes and/or narrow particle size distributions are describedin U.S. Patent Publication No. 2013/0001833 (the “NiedermeyerPublication”), which is incorporated herein by reference.

FIG. 1 is a transmission electron microscope image (TEM) of exemplaryspherical-shaped metal nanoparticles made using the methods and systemsof the Niedermeyer Publication. The illustrated nanoparticles arespherical-shaped silver (Ag) nanoparticles of substantially uniformsize, with a mean diameter of about 10 nm and a narrow particle sizedistribution.

According to some embodiments, the spherical nanoparticles can have asolid core rather than being hollow, as is the case with conventionalmetal nanoparticles, which are usually formed on the surfaces ofnon-metallic seed nanoparticles (e.g., silica), which are thereafterremoved to yield hollow nanospheres. Providing solid rather than hollownanoparticles enhances their ability to be non-covalently andnonionically affixed to a fibrous article surface.

According to some embodiments, spherical-shaped metal nanoparticlesinclude only internal angles and are free of angled edges or externalbond angles, both of which can promote ionization and accumulation ofpoint charges. Such nanoparticles can exhibit a high ξ-potential, whichpermits the spherical nanoparticles to remain dispersed within a polarsolvent without a surfactant, which is a surprising and expected result.In contrast, when point charges are formed, electrostatic forces willthen dominate the interaction between the nanoparticle and the fibrousarticle surface. Once electrostatic forces come into play, theorientation of the nanoparticle relative to the fibrous article surfacewill be wholly determined by those electrostatic forces. Once theseelectrostatic forces are neutralized, whether by surface chemistry,surfactants (detergents), static electrical charges or other externalforces, the adhesive forces holding the particle to the fibrous articlesurface will be lost or even reversed to create a repulsive force andthe interaction between the nanoparticle and the fibrous article surfacewill be lost.

In addition to spherical-shaped metal nanoparticles, it may be desirableto use coral-shaped nanoparticles having controlled particle sizesand/or narrow particle size distributions, such as those described inthe U.S. Provisional Application No. 62/054,126, filed Sep. 23, 2104, inthe name of William Niedermeyer (the “Niedermeyer Application”), andwhich is incorporated herein by reference.

FIGS. 2A-2E are transmission electron microscope images (TEMs) ofexemplary coral-shaped metal nanoparticles made using the methods andsystems of the Niedermeyer Application. Coral-shaped metal nanoparticlescan have a non-uniform cross section and a globular structure formed bymultiple, non-linear strands joined together without right angles.Similar to spherical nanoparticles, coral-shaped nanoparticles with noexternal bond angles or edges can also exhibit a high potential, whichis a surprising and expected result. Coral-shaped nanoparticles can alsobe affixed to fabrics, fibers, filaments, and yarns by Van der Waalsforces similar to spherical-shaped nanoparticles but often not asstrongly, and can impart desired properties to fabrics, fibers,filaments, and yarns. In addition, coral-shaped nanoparticles can assistand/or augment spherical-shaped nanoparticles in becoming uniformlyaffixed to the fabric, fiber, filament, or yarn surface.

The nonionic metal nanoparticles may comprise any desired metal, mixtureof metals, or metal alloy, including at least one of silver, gold,platinum, palladium, rhodium, osmium, ruthenium, rhodium, rhenium,molybdenum, copper, iron, nickel, tin, beryllium, cobalt, antimony,chromium, manganese, zirconium, tin, zinc, tungsten, titanium, vanadium,lanthanum, cerium, heterogeneous mixtures thereof, or alloys thereof.

According to some embodiments, nonionic metal nanoparticles useful formaking nanoparticle treated fibrous articles, such as fabrics, fibers,filaments, and yarns, comprise spherical-shaped nanoparticles,preferably spherical metal nanoparticles having a solid core. In someembodiments, spherical-shaped metal nanoparticles can have a diameter ofabout 40 nm or less, about 35 nm or less, about 30 nm or less, about 25nm or less, about 20 nm or less, about 15 nm or less, about 10 nm orless, about 7.5 nm or less, or about 5 nm or less. In some embodiments,spherical-shaped nanoparticles can have a particle size distributionsuch that at least 99% of the nanoparticles have a diameter within 30%of the mean diameter of the nanoparticles, or within 20% of the meandiameter, or within 10% of the mean diameter. In some embodiments,spherical-shaped nanoparticles can have a mean particle size and atleast 99% of the nanoparticles have a particle size that is within ±3 nmof the mean diameter, ±2 nm of the mean diameter, or ±1 nm of the meandiameter. In some embodiments, spherical-shaped nanoparticles can have apotential of at least 10 mV, preferably at least about 15 mV, morepreferably at least about 20 mV, even more preferably at least about 25mV, and most preferably at least about 30 mV.

According to some embodiments, the nanoparticles may comprisecoral-shaped nanoparticles, e.g., particles that have a non-uniformcross section and a globular structure formed by multiple, non-linearstrands joined together without right angles. Coral-shaped nanoparticlescan have lengths ranging from about 15 nm to about 100 nm, or about 25nm to about 95 nm, or about 40 nm to about 90 nm, or about 60 nm toabout 85 nm, or about 70 nm to about 80 nm. Coral-shaped nanoparticlescan have a particle size distribution such that at least 99% of thenanoparticles have a length within 30% of the mean length, or within 20%of the mean length, or within 10% of the mean length. In someembodiments, coral-shaped nanoparticles can have a ξ-potential of atleast 10 mV, preferably at least about 15 mV, more preferably at leastabout 20 mV, even more preferably at least about 25 mV, and mostpreferably at least about 30 mV.

In some embodiments, the nanoparticle treated fibrous article mayinclude both spherical-shaped and coral-shaped nanoparticles (e.g., thespherical-shaped nanoparticles may comprise silver nanoparticles and thecoral-shaped nanoparticles may comprise gold nanoparticles). Accordingto one embodiment, spherical-shaped nanoparticles consist essentially orentirely of silver (Ag) nanoparticles. In the case where coral-shapednanoparticles are used, they may consist essentially or entirely of gold(AU) nanoparticles. In some embodiments, spherical-shaped nanoparticlescan comprise an alloy or mixture of silver and gold.

The nanoparticle composition may include only spherical-shaped metalnanoparticles, only coral-shaped metal nanoparticles, or bothspherical-shaped and coral-shaped metal nanoparticles. In some cases,the spherical-shaped metal nanoparticles are more strongly affixed tothe fibrous article than the coral-shaped metal nanoparticles.Nevertheless, the coral-shaped metal nanoparticles may assist inaffixing the spherical-shaped metal nanoparticles to the fibrousarticle. In some embodiments, the mass ratio of spherical-shapednanoparticles to coral-shaped nanoparticles in for treatment onto afabric or fiber can be in a range of about 1:1 to about 50:1, or about2.5:1 to about 25:1, or about 5:1 to about 20:1, or about 7.5:1 to about15:1, or about 9:1 to about 11:1, or about 10:1. The particle numberratio of spherical-shaped nanoparticles to coral-shaped nanoparticles infor treatment onto a fabric or fiber can be in a range of about 10:1 toabout 500:1, or about 25:1 to about 250:1, or about 50:1 to about 200:1,or about 75:1 to about 150:1, or about 90:1 to about 110:1, or about100:1.

Releasable Affixation to Fibrous Articles

An advantage of spherical or essentially spherical nanoparticles is thatthey can approach a fabric, fiber, filament, or yarn surface withoutlocalized point charge forces. This allows the nanoparticle to comewithin the range of Van der Waals forces, with the overall forceincreasing inversely relative to the distance between the nanoparticleand the fibrous article surface. Empirical tests verify the strength ofthe adhesive forces between the nanoparticles and the fibrous articlesurface, with tests demonstrating that the nanoparticles remain affixedto the fibrous article surface through routine uses, including appliedfrictional forces, multiple wash cycles using standard fabricdetergents, and heat from a clothes dryer (in excess of 50 wash anddrying cycles).

By way of example, a fabric containing spherical-shaped nanoparticlesaffixed to a surface was subjected to 50 wash and dry cycles in aconventional washer and dryer. No ionic silver (Ag⁺) was detected in thewash water. Because the spherical-shaped nanoparticles were firmlyaffixed to the fabric without covalent bonds and ionic bonds and withoutbeing embedded within the fabric or a within a coating matrix, yet ableto withstand being removed when washed and heat dries, it is postulatedthat they are nonionic, have no point charges, and are affixed to thefabric, fiber, filament, or yarn by Van der Waals forces.

FIG. 3 schematically illustrates a nanotreated fabric, fiber, filament,or yarn 400, which includes a fibrous article surface 402 and aplurality of spherical-shaped nanoparticles 404 affixed thereto. Thespherical-shaped nanoparticles 404 are preferentially affixed to thefibrous article surface 402 in a substantially uniform concentration ordistribution in order to provide similar properties throughout thefibrous article. According to some embodiments, the concentration ofnanoparticles is generally about 0.1 mg to about 1 mg per yard offabric.

FIG. 4 is a theoretical model showing a spherical-shaped metalnanoparticle strongly affixed to a fibrous article surface 502 withoutcovelent or ionic bonds. It is postulated that when an exposed,nonionic, spherical-shaped metal nanoparticle 504 is within a distance D(e.g., about 35 nm for a silver (Ag) nanoparticle) of fibrous articlesurface 502, the surface 502 “sees” the nanoparticle as a flat elongatedsurface rather than a sphere. If the spherical-shaped metal nanoparticle504 interacted with the fibrous article surface 502 as a sphere ratherthan a flat surface, only the few atoms of the spherical nanoparticlenearest the fibrous article surface 502 would be attracted by Van derWaals forces, and the forces acting on the other atoms would drop offquickly. In that case, the relatively high mass of the nanoparticlewould overcome and overwhelm the relatively small Van der Waals forcesapplied to the closest atoms and the nanoparticle would easily fall off.However, because nanoparticle 504 is instead tightly affixed to fibrousarticle surface 502, nanoparticle 504 apparently interacts with surface502 in a way so as to be “seen” as an enlarged flat surface. The Van derWaals forces act with essentially equal attractive force to the entireflat surface, which greatly enhances the magnitude of the attractive Vander Waals forces acting to affix nanoparticle 504, and nanoparticle 504is instead tightly affixed to fibrous article surface 502. This has beenempirically shown to be true. Moreover, mathematical calculationspredict that solid, spherical metal nanoparticles can behave andinteract with a surface in the manner depicted in FIG. 4.

Active Transport Mechanisms

The nanoparticle treated fibrous article can be coated with a generallyeven distribution of nanoparticles, which will remain on the fibrousarticle surface until an active absorption or other transport mechanismis presented that is capable of overcoming the attractive forces. Activeabsorption or other transport mechanism results when a microbe, such asa virus, bacterium or fungus, comes into contact with the nanoparticletreated fibrous article such that the microbe physically contacts atleast one nanoparticle. Because an individual nanoparticle is so muchsmaller than the microbe, particularly bacteria and fungi, microbesactively absorb materials from their environment, and individualnanoparticles are not covalently bonded to or physically incorporatedinto the fibrous structure of the article, the nanoparticles can beactively absorbed or transported from the surface of the fibrous articleinto the microbe where appropriately chosen particles can then kill orinactivate the microbe.

Although nanoparticles tightly held to a fibrous article surface by Vander Waals forces have been shown to withstand typical environmentalforces and will remain on the fibrous article surface through normalactivities, the attractive forces between the nanoparticles and fibrousarticle surface are not permanent and insurmountable, such as in acovalent bond or where the particles are bound within the structure ofthe fabric or a matrix of a coating. As a result, the adhesive forcesaffixing the nanoparticles can be overcome and the nanoparticles can bereleased when the particles interact with other surfaces that present anactive transport mechanism, such as bacteria, fungi, or even viruses.Such microbes have different cellular compositions and cell wallfunctions than those typical of human and mammalian cells, such as hairand skin that typically would come in contact with a fabric, fiber,filament, or yarn.

FIG. 5 schematically illustrates a proposed model by which a microbe 608approaching a fibrous article surface 602 with spherical-shapednanoparticles 604 affixed thereto can remove one or more of thespherical-shaped nanoparticles 604 from fibrous article surface 602,such as by active absorption or other transport mechanism. The removednanoparticles 604 can freely move throughout the interior 606 of microbe608 and come into contact with one or more vital proteins or enzymes 610that, if denatured, will kill or disable the microbe.

Antimicrobial Activity

One way that nanoparticles may kill or denature a microbe is bycatalyzing the cleavage of disulfide (S—S) bonds within a vital proteinor enzyme. FIG. 6 schematically illustrates a microbe protein or enzyme710 with disulfide bonds being catalytically denatured by an adjacentspherical-shaped nanoparticle 704 to yield denatured protein or enzyme712. In the case of bacteria or fungi, the cleavage of disulfide bondsand/or cleavage of other chemical bonds of vital proteins or enzymes mayoccur within the cell interior, thereby killing the microbe in thismanner Such catalytic cleavage of disulfide (S—S) bonds is facilitatedby the generally simple protein structures of microbes, in which manyvital disulfide bonds are exposed and readily cleaved by catalysis.

Another mechanism by which metal (e.g., silver) nanoparticles can killmicrobes is through the production of active oxygen species, such asperoxides, which can oxidatively cleave protein bonds, including but notlimited to amide bonds.

In the case of viruses, spherical-shaped and coral-shaped metalnanoparticles can deactivate viruses by attaching to glycoproteinsand/or catalyzing protein denaturing reactions in the protein coat sothat the virus is no longer able to attach to a host cell and/or injectgenetic material into the host cell. Because very small nanoparticlescan pass through a virus, denaturing of the protein coat may occurwithin the interior of the virus. A virus that is rendered unable toattach to a host cell and/or inject genetic material into the host cellis essentially inactive and no longer pathogenic.

Notwithstanding the lethal nature of nonionic metal nanoparticlesrelative to microbes, they can be relatively harmless to humans,mammals, and healthy mammalian cells, which contain much more complexprotein structures compared to simple microbes in which most or allvital disulfide bonds are shielded by other, more stable regions of theprotein. FIG. 7 schematically illustrates a mammalian protein 810 withdisulfide (S—S) bonds that are shielded so as to resist beingcatalytically denatured by an adjacent spherical-shaped nanoparticle804. In many cases the nonionic nanoparticles do not interact with orattach to human or mammalian cells, remain in and follow fluid flow, donot cross barriers, remain in the vascular system, and can be quicklyand safely expelled through the urine without damaging kidneys or othercells.

In the particular case of silver (Ag) nanoparticles, the interaction ofthe silver (Ag) nanoparticle(s) within a microbe has been demonstratedto be particularly lethal without the need to rely on the production ofsilver ions (Ag⁺) to provide the desired antimicrobial effects, as istypically the case with conventional colloidal silver treatments offabrics. In addition, the ability of affixed metal nanoparticles to bepreferentially released directly into microbial cells minimized therelease of potentially toxic metal cations into the local and largerenvironment. The ability of silver (Ag) nanoparticles to be affixed tofibrous articles while providing effective microbial control without anysignificant release of toxic silver ions (Ag⁺) into the surroundingenvironment is a substantial advancement in the art.

The size of the particles can be selected to target and kill specifictypes of microbes. For example, nanoparticle may be size optimized toselectively target and kill certain microbes. By way of example,nanoparticles having a diameter of less than about 8 nm (e.g., about 1-7nm, or about 2-6.5 nm, or about 3-6 nm) have been found to be effectivein killing viruses, nanoparticles having a diameter of about 3-14 nm(e.g., about 5-13 nm, or about 7-12 nm, or about 8-10 nm) have beenfound to be effective in killing bacteria, and nanoparticles having adiameter of about 9-20 nm (e.g., about 10-18 nm, or about 11-16 nm, orabout 12-15 nm) have been found to be effective in killing fungi. Withinthe foregoing ranges, there may be specific sizes of nanoparticles thatare most effective in killing a particular type of virus, bacterium, orfungus. For example, sub-micron sized metal nanoparticles (e.g., goldnanoparticles having a diameter of about 0.4 nm) may be most effectivein killing ebola viruses due their oddly elongated and loopedconfiguration.

Other Exemplary Beneficial Properties

In addition to providing fibrous articles, such as fabrics, fibers,filaments, and yarns, with antimicrobial properties, which reduces oreliminates odors and kills potentially dangerous pathogens, thenanoparticles can also impart high temperature transfer properties,yielding clothing and other fibrous articles (such as animal hair orfur) that feel cooler to the wearer or animal. Fibrous articles(including animal hair or fur) treated with nonionic metal nanoparticlesas disclosed herein can have improved thermodynamic heat transferproperties, such as increased convection (e.g., increased waterevaporation) and increased thermal emissivity (e.g., radiation of heat).Nanoparticle treated fabrics and other fibrous articles (includinganimal hair or fur) can move heat faster to the surrounding environmentthan untreated fabrics. In addition, while nanoparticle treated fibrousarticles as disclosed herein provide improved convection propertiessimilar to conventional fabrics treated with colloidal silver, theincrease in thermal emissivity requires, and is only provided by,spherical-shaped and/or coral-shaped nanoparticles of narrow particlesize distribution. This is a surprising and unexpected result.

In some embodiments, a nanoparticle treated fabric exhibits anti-odorproperties. For example, some embodiments include a plurality of silvernanoparticles providing anti-microbial functionality (which reduces oreliminates microbial production of odor causing molecules) and aplurality of gold nanoparticles providing an additional, independentsource of anti-odor functionality (e.g., by catalyzing the disruption ofamines, sulfides, organic molecules, and other odorous molecules).

In some embodiments, a nanoparticle treated fabric exhibits improveddurability and colorfast properties. For example, some embodimentsinclude a plurality of nanoparticles (e.g., gold nanoparticles)configured to induce a phase shift (e.g., toward the red end of thespectrum) of ultraviolet light incident upon the treated fabric. Theassociated protection from ultraviolet light can beneficially improvethe strength, durability, and color-fastness of the nanoparticle treatedfabric.

In some embodiments, a nanoparticle treated fabric exhibits improveddrying/moisture removal properties. For example, the nanoparticles of ananoparticle treated fabric can provide an increased surface area fordrying and/or can alter the emissivity of the treated fabric, therebyleading to greater removal of moisture from the treated fabric.

In some embodiments, a nanoparticle treated material exhibits radiationprotection properties. For example, some embodiments include a pluralityof nanoparticles (e.g., beryllium and/or gold) configured to absorbharmful radiation (e.g., alpha particles, beta particles, and/or gammaradiation), thereby reducing or eliminating an amount of radiationpassing through the nanoparticle treated material.

In some embodiments, a nanoparticle treated material decreases oreliminates visibility to radar, infrared, and/or other detectionmethods. For example, some embodiments include a plurality ofnanoparticles (e.g., cobalt nanoparticles) configured to absorb radarand/or other detection signals, thereby rendering the nanoparticletreated material invisible or less visible to detection.

In some embodiments, a nanoparticle treated material is formed as anelectrically conductive material. For example, a plurality of conductivemetal nanoparticles can be embedded within a fibrous article to providethe fibrous article with electrically conductive properties. Theconductive properties can be tuned by adjusting the type and compositionof the nanoparticles used, the concentration of the nanoparticles,and/or the distribution of nanoparticles throughout the fibrous article,for example. In one embodiment, a conductive fibrous article can be usedin applications for detecting a break in a fiber and/or the level ofbreakage in a collection of fibers based on changes in conductivity ofthe material.

Methods of Manufacture and Use

According to some embodiments, a method of manufacturing a nanoparticletreated fibrous article comprises: (1) applying a nanoparticlecomposition comprised of a liquid carrier and a plurality of nonionicmetal nanoparticles to a fibrous article, such as an animal's fur orhair, a fabric, fiber, filament, or yarn, and (2) removing the liquidcarrier to yield a nanoparticle treated fibrous article in which thenonionic metal nanoparticles are exposed and non-covalently affixed tothe fibrous article. In some embodiments, at least a portion of thenonionic metal nanoparticles can be non-covalently affixed to thefibrous article by Van der Waals forces.

According to some embodiments, the liquid carrier comprises one or moreof a non-polar liquid, an organic solvent, a polar liquid, or an aqueousliquid. Examples of suitable liquid carriers include water, methanol,ethanol, isopropyl alcohol, other alcohols, acetone, ketones, aldehydes,and ethyl acetate.

In some cases it may be desirable for the liquid carrier to be volatileso that when applying the nanoparticle composition to a fibrous articlethe volatile liquid carrier can be removed by evaporation rather thanrunning through or past the surface being treated, which can carry thenanoparticles away and prevent adherence to the surface. According tosome embodiments, the volatile liquid carrier is advantageously removedby evaporation while applying the nanoparticle composition to thefibrous article. For example, the nanoparticle composition can beapplied to a fabric or other fibrous article by dry fogging.Alternatively, the nanoparticle composition can be applied by dipping,followed by fast drying of the volatile liquid in order to leave behindsufficient nanoparticle residue. The application process can be repeatedto yield a fabric or other fibrous article having a desiredconcentration of nanoparticles.

According to some embodiments, a nanoparticle composition comprised ofethanol and spherical metal nanoparticles, and devoid of any surfactant,is applied to a fabric or other fibrous article by spraying andsimultaneous evaporation of the ethanol in order to coat the fabric orother fibrous article surface with spherical metal nanoparticles, thespherical metal nanoparticles being strongly affixed by Van der Waalsforces. According to another embodiment, coral-shaped metalnanoparticles can additionally or alternatively be included in order tohelp carry and attach the spherical metal nanoparticles to the fabric orother fibrous article surface. After application and drying of thesolvent, coral-shaped metal nanoparticles may be attached less stronglyto the fibrous article compared to spherical-shaped metal nanoparticles.In some cases it may be possible to selectively remove coral-shapednanoparticle, e.g., for reuse, while leaving spherical-shapednanoparticles in place.

In some embodiments, a plurality of nanoparticles can be added to amasterbatch prior to processing of the masterbatch into fibers, fabrics,upholsteries, yarns, filaments, etc. (e.g., for polyesters, nylons,acrylics, and other synthetic fabrics). In such embodiments, thenanoparticles added to the masterbatch can be embedded in the resultingfabric. In some embodiments, the nanoparticles may be added to themasterbatch by mixing the nanoparticles in an ethylene glycol carrier orsimilar carrier (e.g., other alcohols and particularly other diols), andadding the resulting solution to the masterbatch. The resulting solutioncan have a concentration of nanoparticles with a lower bound of about 1ppm, 3 ppm, 5 ppm, 10 ppm, 15 ppm, or 25 ppm, and an upper bound ofabout 50 ppm, 100 ppm, 200 ppm, 300 ppm, 400 ppm, or 500 ppm, or mayhave a concentration within a range of any of the foregoing upper andlower bounds, for example.

In some embodiments, a method of manufacture in which the nonionic metalnanoparticles are exposed and non-covalently affixed to the fibrousarticle can be useful for antimicrobial applications or otherapplications where it may be beneficial for at least some of the metalnanoparticles to be detachably affixed to the treated fibrous article,for example. In some embodiments, a method of manufacture in which atleast some of the nonionic metal nanoparticles are embedded in thefibrous article (e.g., are mixed with a masterbatch prior to processingof the masterbatch) can be useful for anti-radiation, anti-radar, and/orelectrically conductive fabric applications, for example. The foregoingmethods of manufacture can be combined, altered, and/or adjusted to meetneeds and preferences.

According to some embodiments, a method of using a nanoparticle treatedfibrous article comprises: (1) providing a nanoparticle treated fibrousarticle, such as a nanoparticle treated fabric, fiber, filament, oryarn, as described herein; (2) exposing the nanoparticle treated fibrousarticle to microbes; (3) the microbes selectively removing a portion ofthe exposed, nonionic metal nanoparticles from the fibrous article; and(4) the metal nanoparticles killing or denaturing the microbes.

The nanoparticle treated fibrous article can be further exposed to oneor more of water, soap, surfactant, or solvent; however, the metalnanoparticles can remain attached to the fibrous article except whencontacted by a microbe. In the case where the metal nanoparticlescomprise both spherical-shaped and coral-shaped nanoparticles,spherical-shaped metal nanoparticles can be more strongly affixed to thefibrous article surface than coral-shaped metal nanoparticles. Whenexposing the nanoparticle treated fibrous article to one or more ofwater, soap, surfactant, or solvent, the spherical-shaped metalnanoparticles can remain attached to the fabric, fiber, filament, oryarn except when contacted by a microbe, and at least a portion of thecoral-shaped metal nanoparticles can be more easily removed by the oneor more of water, soap, surfactant, or solvent.

EXAMPLES Example 1

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 1 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a distilled water solution forapplication onto polyester fabric utilizing a dry fog system.

Example 2

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 2 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a distilled water solution forapplication onto cotton fabric utilizing a dry fog system.

Example 3

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 5 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a distilled water solution forapplication onto polyester fabric utilizing a dry fog system.

Example 4

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 10 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a distilled water solution forapplication onto cotton fabric utilizing a dry fog system.

Example 5

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 1 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 5% ethanol 95% distilled watersolution for application onto cotton fabric utilizing a dry fog system.

Example 6

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 2 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 5% ethanol 95% distilled watersolution for application onto polyester fabric utilizing a dry fogsystem.

Example 7

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 5 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 5% ethanol 95% distilled watersolution for application onto polyester fabric utilizing a dry fogsystem.

Example 8

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 10 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 5% ethanol 95% distilled watersolution for application onto cotton fabric utilizing a dry fog system.

Example 9

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 1 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 95% ethanol solution for applicationonto cotton fabric utilizing a dry fog system.

Example 10

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 2 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 95% ethanol solution for applicationonto polyester fabric utilizing a dry fog system.

Example 11

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 5 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 95% ethanol solution for applicationonto polyester fabric utilizing a dry fog system.

Example 12

To manufacture a nanoparticle treated fabric, 1 mg/L of 25 nmspherical-shaped gold (Au) nanoparticles, 1 mg/L of 70 nm coral-shapedgold (Au) nanoparticles, and 10 mg/L of 10 nm spherical-shaped silver(Ag) nanoparticles were put into a 95% ethanol solution for applicationonto cotton fabric utilizing a dry fog system.

Example 13

Metal nanoparticles (25 nm spherical-shaped gold particles) are added todistilled water at concentrations of 1 mg/L, 5 mg/L, and 10 mg/L to formseparate treatment solutions. The resulting solutions are readilyapplied to the hair or fur of an animal via spraying or dry fogging tocool the animal. Some portion of the nanoparticles can also be appliedto the animal's skin and provide cooling thereof.

Example 14

Metal nanoparticles (70 nm coral-shaped gold particles) are added todistilled water at concentrations of 1 mg/L, 5 mg/L, and 10 mg/L. Theresulting solutions are readily applied to the hair or fur of an animalvia spraying or dry fogging to cool the animal. Some portion of thenanoparticles can also be applied to the animal's skin and providecooling thereof.

Example 15

Metal nanoparticles (25 nm spherical-shaped gold particles) are added tosolutions of 5 to 95% ethanol (remainder water) at concentrations of 1mg/L, 5 mg/L, and 10 mg/L to form separate treatment solutions. Theresulting solutions are readily applied to the hair or fur of an animalvia spraying or dry fogging to cool the animal. Some portion of thenanoparticles can also be applied to the animal's skin and providecooling thereof.

Example 16

Metal nanoparticles (70 nm coral-shaped gold particles) are added tosolutions of 5 to 95% ethanol (remainder water) at concentrations of 1mg/L, 5 mg/L, and 10 mg/L. The resulting solutions are readily appliedto the hair or fur of an animal via spraying or dry fogging to cool theanimal. Some portion of the nanoparticles can also be applied to theanimal's skin and provide cooling thereof.

The present invention may be embodied in other specific forms withoutdeparting from its spirit or essential characteristics. The describedembodiments are to be considered in all respects only as illustrativeand not restrictive. The scope of the invention is, therefore, indicatedby the appended claims rather than by the foregoing description. Allchanges which come within the meaning and range of equivalency of theclaims are to be embraced within their scope.

What is claimed is:
 1. A method of treating a fibrous material toprovide effective cooling of the fibrous material, the methodcomprising: providing a fibrous material; applying a nanoparticlecomposition to the fibrous material, the nanoparticle composition beingcomprised of a plurality of nonionic metal nanoparticles, and a liquidcarrier; removing the liquid carrier such that the nonionic metalnanoparticles remain exposed and non-covalently affixed to the fibrousmaterial; and the nonionic metal nanoparticles affecting the heattransfer properties of the treated fibrous material to provide effectivecooling of the fibrous material.
 2. The method of claim 1, wherein thefibrous material is from an animal source.
 3. The method of claim 2,wherein the fibrous material is fur or hair of an animal.
 4. The methodof claim 3, wherein the fur or hair of the animal is attached to aliving animal.
 5. The method of claim 4, wherein a portion of thenanoparticle composition is applied to skin of the living animal.
 6. Themethod of claim 1, wherein the nonionic metal nanoparticles comprise atleast one metal selected from the group consisting of silver, gold,platinum, palladium, rhodium, osmium, ruthenium, rhodium, rhenium,molybdenum, copper, iron, nickel, tin, beryllium, cobalt, antimony,chromium, manganese, zirconium, tin, zinc, tungsten, titanium, vanadium,lanthanum, cerium, heterogeneous mixtures thereof, and alloys thereof.7. The method of claim 1, wherein the nonionic metal nanoparticlescomprise gold nanoparticles.
 8. The method of claim 1, wherein thenonionic metal nanoparticles have a mean diameter or length and whereinat least 99% of the metal nanoparticles have a diameter or length within30% of the mean diameter or length.
 9. The method of claim 1, whereinthe nonionic metal nanoparticles have a ξ-potential of at least 10 mV.10. The method of claim 1, wherein the nonionic metal nanoparticlesincludes spherical-shaped nanoparticles having a solid core and adiameter of 40 nm or less.
 11. The method of claim 9, wherein thespherical-shaped nanoparticles have a mean diameter and wherein at least99% of the spherical-shaped nanoparticles have a diameter within ±3 nmof the mean diameter.
 12. The method of claim 1, wherein at least aportion of the nonionic metal nanoparticles are non-covalently affixedto the fibrous material by Van der Waals forces.
 13. A method oftreating an animal to provide effective cooling of the animal, themethod comprising: providing an animal; applying a nanoparticlecomposition to the fur, hair, or feathers of the animal, thenanoparticle composition being comprised of a plurality of nonionicmetal nanoparticles, the plurality of metal nanoparticles including goldnanoparticles, and a liquid carrier; removing the liquid carrier suchthat the nonionic metal nanoparticles remain exposed and non-covalentlyaffixed to the fur or hair of the animal; and the nonionic metalnanoparticles affecting the heat transfer properties of the treated furor hair to provide effective cooling of the animal.
 14. The method ofclaim 13, wherein the treated animal is a livestock animal.
 15. Themethod of claim 13, wherein the nonionic metal nanoparticles includespherical-shaped nanoparticles.
 16. The method of claim 13, wherein thenonionic metal nanoparticles include coral-shaped nanoparticles.
 17. Ananoparticle treated fibrous article from an animal source, thenanoparticle treated fibrous article having heat transfer propertiesthat provide more effective heat transfer than an article untreated withnanoparticles, the article comprising: a fibrous article from an animalsource; and a plurality of exposed, nonionic metal nanoparticlesnon-covalently affixed to the fibrous article.
 18. A nanoparticletreated fibrous article as in claim 17, wherein the fibrous article isfur or hair of an animal attached to a living animal.
 19. A nanoparticletreated fibrous article as in claim 17, wherein the animal is alivestock animal.
 20. A nanoparticle treated fibrous article as in claim17, wherein the nonionic metal nanoparticles are selected from the groupconsisting of gold, silver, heterogenous mixtures thereof, and alloysthereof.